# TBC Solar Cell Technology (TOPCon Back Contact): Full Process Guide - - Ooitech, the world's leading solar panel production line solutions provider, supply chain expert, solar panel making machine facotry > A detailed walkthrough of TBC (TOPCon Back Contact / POLO-IBC) solar cell technology, covering its structure, complete process flow, and the key control points that matter most in production. ![TBC Solar Cell Technology (TOPCon Back Contact): Full Process Guide](https://cdn.ooitech.com/static/upload/image/20260712/b328022a0ca3c179e39311d2ccf4fb5d.webp) - ** 2026-07-12 - ** 0 Views - ** [Blog](/Blog.html) ### TBC Solar Cell Technology (TOPCon Back Contact): Full Process Guide ##### Technology Overview The content below is shared for reference only. If there is any technical infringement or incorrect guidance, feel free to contact the author for removal or correction. ###### What is a TBC cell? TBC stands for TOPCon Back Contact. It fuses TOPCon passivation (tunnel oxide plus poly-silicon) with the IBC interdigitated back contact structure, so people also call it a POLO-IBC cell. It deep-integrates the TOPCon tunnel oxide / poly-Si passivation with the IBC back contact layout. That gives you the strong rear passivation of TOPCon plus the IBC advantage of no front gridline shading, with all current collection moved to the back. The result is higher open-circuit voltage and higher short-circuit current. It's one of the mainstream N-type high-efficiency routes for the next generation. ###### Core advantages - No front metal gridlines, so front shading loss is removed and Isc goes up - TOPCon tunnel passivation lowers rear recombination and lifts Voc - The interdigitated P/N back contact layout optimizes the carrier collection path and cuts series resistance - Compared with standard TOPCon and standard IBC, it balances passivation quality and structural integration - Compatible with most core equipment on existing N-type lines, so the process can be upgraded step by step ###### How it compares with conventional cells - Standard TOPCon: front gridline shading, full-area TOPCon passivation on the rear - Standard IBC: back contact structure, but passivation relies on silicon oxide / silicon nitride, no tunnel poly-Si passivation - TBC (POLO-IBC): IBC back contact structure plus integrated TOPCon tunnel passivation, so both structure and passivation are optimized ##### Full Process Flow Overview Wafer incoming → pre-cleaning / saw damage removal → rear tunnel oxide + poly-Si deposition (LPCVD) → rear SiN mask deposition → first rear laser opening (boron area) → boron doping (p-poly) → second rear laser opening (phosphorus area) → phosphorus doping (n-poly) → cleaning to strip wrap-around diffusion / BSG / PSG → rear passivation film deposition → wax mask printing to protect the rear → front texturing + P/N isolation etch → front and rear SiN anti-reflection passivation film deposition → rear metal electrode screen printing → firing → electrical test → sorting and packing ##### Detailed Process Specifications ###### 3.1 Cleaning and polishing (pre-clean + saw damage removal) Purpose: remove the saw damage layer, surface metal impurities, particles and oil; polish the wafer single or double sided to get a clean, flat silicon base and keep the later tunnel layer deposition uniform. Main equipment: inline wet cleaning and polishing line, alkaline polishing tank, acid cleaning tank. Key chemicals: strong alkali (NaOH/KOH), HF, HCl, IPA, texturing additive, surfactant. Key monitoring items: - Polishing weight loss: electronic balance - Surface reflectance: reflectance tester - Minority carrier lifetime iVoc: WCT-120 transient lifetime tester - Carrier recombination imaging: PL tester (R3-PL) - Surface roughness and cleanliness: optical microscope Quality control: saw damage fully removed, no stains or steps on the surface, uniform weight loss, no obvious lifetime drop. ###### 3.2 Tunnel oxide + poly-Si deposition Purpose: grow an ultra-thin tunnel oxide (SiO₂) then an intrinsic poly-Si layer on the wafer rear, forming the core TOPCon passivation structure for strong field and chemical passivation and low rear recombination. Main equipment: tube LPCVD. Gas sources: SiH₄, O₂, N₂ (carrier / purge). Key items: - Poly-Si thickness: poly thickness tester, ellipsometer - Tunnel oxide thickness: ECV, ellipsometer - iVoc (WCT-120) - PL uniformity - Sheet resistance (intrinsic poly monitoring before doping) Quality control: oxide ultra-thin and uniform, poly-Si dense and pinhole-free, good thickness consistency across the wafer. ###### 3.3 Rear SiN mask deposition Purpose: deposit a dense silicon nitride (SiNₓ) layer on the intrinsic poly-Si as a blocking mask for the later laser opening and doping steps, enabling selective doping zones. Main equipment: PECVD. Gas sources: SiH₄, NH₃, N₂. Key items: SiN thickness (spectroscopic ellipsometer), refractive index and uniformity, iVoc, PL uniformity. Quality control: dense mask, no pinholes, uniform thickness to guarantee doping isolation. ###### 3.4 First rear laser opening (boron diffusion window) Purpose: selectively remove the SiN mask over the boron diffusion area by local laser ablation while keeping the intrinsic poly-Si underneath, opening the window for the later p-type poly. Main equipment: fiber / nanosecond or picosecond laser opening system, high-precision laser patterning tool. Process tuning: adjust laser power, repetition rate, scan speed and spot overlap so only the top SiN mask is removed and the intrinsic poly-Si below is not damaged, keeping the passivation base intact. Key characterization: optical microscope check of groove shape, edge integrity, and whether the poly layer is burned. ###### 3.5 Rear boron doping (p-poly) Purpose: boron-diffuse the intrinsic poly-Si in the opened area to convert it into p-type heavily doped poly (p-poly), while forming BSG on the surface. The BSG later acts as a natural blocking mask for phosphorus diffusion. Main equipment: tube boron diffusion furnace. Process media: liquid source BBr₃; ambient O₂, N₂. Key characterization: p-zone sheet resistance, doping uniformity, BSG coverage integrity, PL doping uniformity. Quality control: sufficient boron doping, uniform sheet resistance, continuous and complete BSG with no local gaps. ###### 3.6 Second rear laser opening (phosphorus diffusion window) Purpose: remove the remaining SiN mask to expose the undoped intrinsic poly-Si as the n-type phosphorus doping zone, while keeping the already formed BSG layer intact from laser damage. Main equipment: laser patterning / opening system. Process focus: precise laser energy control to avoid punching through the BSG layer, keeping a clean isolation boundary between P and N zones. ###### 3.7 Rear phosphorus doping (n-poly) Purpose: phosphorus-diffuse the second-window intrinsic poly-Si to form n-type heavily doped poly (n-poly). The BSG formed in the previous step works as a self-aligned mask, blocking phosphorus from diffusing into the p-poly area and achieving self-isolation of the P/N zones. Main equipment: tube phosphorus diffusion furnace. Process media: liquid source POCl₃; ambient O₂, N₂. Key principle: the residual BSG acts as a natural diffusion barrier and stops phosphorus contamination of the p-poly area. After phosphorus diffusion the BSG partly turns into a boron-phosphorus mixed oxide, which further strengthens the isolation. Key characterization: n-zone sheet resistance, P/N boundary isolation, leakage trend monitoring. ###### 3.8 Cleaning to strip wrap-around diffusion (BSG/PSG removal) Purpose: chemically remove all BSG, PSG and surface residues, and strip the edge wrap-around and side doping layers to avoid edge leakage. Main equipment: inline wet cleaning line. Key chemicals: mainly HF, plus acidic additives and a buffered acid system. Process aids: clean dry air blow-off, hot air drying. Quality control: oxide glass fully removed, clean surface with no residue, no wrap-around residue at the edges. ###### 3.9 Rear SiN passivation protective film deposition Purpose: deposit a SiN passivation protective film on the rear interdigitated P/N poly structure to passivate and protect the back contact area and block chemical attack in later steps. Main equipment: PECVD. Gas sources: SiH₄, NH₃, N₂. Characterization: SiN thickness, refractive index, film uniformity. ###### 3.10 Rear wax mask coating (protective mask) Purpose: fully coat the rear with a wax protective layer by screen printing to shield the formed P/N back contact structure and SiN film, preventing the later front etch from attacking the rear functional layers. Main equipment: screen printer (wax printing station). Control focus: complete wax printing, no skip printing, no pinholes, good edge sealing so the rear stays protected throughout. ###### 3.11 Front chemical etching + wax stripping and cleaning Purpose: 1. Remove excess doping and damage layers on the wafer front 2. Texture the front to form a pyramid surface and cut front reflection 3. Achieve edge isolation between the rear P and N zones through lateral etching to reduce edge leakage 4. Finally strip the rear wax mask to expose the complete back contact structure Main equipment: double-sided inline wet etching and texturing line. Key chemicals: strong alkali (NaOH), HF, texturing additive, buffered etchant. Gas sources: clean compressed air, N₂ blow-off. Quality control: uniform front texturing, qualified pyramid morphology, proper P/N isolation, no leakage path, clean wax stripping with no residue. ###### 3.12 Front and rear SiN anti-reflection passivation film Purpose: deposit a SiN anti-reflection passivation film on the front for both anti-reflection and surface passivation; add and optimize the rear passivation film to further improve passivation and reliability. Main equipment: PECVD. Gas sources: SiH₄, NH₃, N₂. Characterization: front and rear film thickness, refractive index, minority carrier lifetime, reflectance. ###### 3.13 Rear electrode screen printing and firing Purpose: print silver-aluminum electrodes on the rear P zone and silver electrodes on the n-type poly zone to form the interdigitated back contact positive and negative electrodes, then use high-temperature firing to form ohmic contact between the metal and the doped poly-Si. Main equipment: dedicated back contact screen printer, inline firing furnace. Key steps: rear electrode pattern alignment printing → drying → high-temperature firing (forming ohmic contact). ###### 3.14 Back-end inspection and sorting Process content: EL inspection (defects, micro-cracks, leakage), IV electrical test (Voc, Isc, FF, Eff), appearance inspection, grading and sorting, packing and warehousing. Inspection equipment: EL tester, IV tester, appearance inspection station. ##### Key Challenges and What to Focus On What are the tough parts of TBC technology, and where should attention go? - Controlling the thickness uniformity of the ultra-thin tunnel oxide is hard - The two laser opening steps demand extremely high alignment accuracy - Keeping the BSG self-aligned mask intact is the core of the process - The P/N interdigitated isolation etch is prone to edge leakage - Back contact electrode printing needs higher alignment accuracy than conventional cells - Managing minority carrier lifetime decay across the whole flow is difficult ###### Key SPC parameters to watch - Tunnel oxide thickness and poly-Si thickness - Laser opening morphology and alignment deviation for both steps - Sheet resistance uniformity of boron and phosphorus diffusion - iVoc and PL minority carrier lifetime tracked across the whole flow - Front reflectance and texturing morphology - EL micro-cracks, leakage, and edge isolation status ##### Ooitech's View TBC lives or dies on the details, and the BSG self-aligned mask is the quiet hero here since it lets phosphorus and boron zones sort themselves out without a third mask step. What we watch most on module lines is how these high-Voc back contact cells behave downstream in stringing and lamination, because their all-rear metallization changes the interconnection game. If you want to see real N-type module lines running, our YouTube channel [www.youtube.com/ooitech](http://www.youtube.com/ooitech) has factory footage worth a look. --- ##### Tags : ![](/template/ooitech/assets/img/shape/06.png) ![](https://cdn.ooitech.com/static/upload/image/20250909/1757399770541443.webp) ### Request A Quote All uploads are secure and confidential. ## We deliver expertise you can trust our service Direct-from-Factory Equipment. ![](/template/ooitech/assets/img/icon/money-2.svg) ### Cost-Effective Advantages We deliver exceptional value, maximizing results while optimizing budgets for clients. ![](/template/ooitech/assets/img/icon/staff.svg) ### Our Experience Team Our skilled professionals specialize in innovative solutions and tailored strategies. ![](/template/ooitech/assets/img/icon/certified.svg) ### 15+ Years Industry Experience Deep expertise ensures reliable, trend-aware, and proven outcomes for success. ![](https://cdn.ooitech.com/static/upload/image/20250910/1757477357667605.webp ) ![](https://cdn.ooitech.com/static/upload/image/20250910/1757477724911512.webp) ![](/template/ooitech/assets/img/shape/06.png) ## What Our Client Say's about us Client testimonials praise our deep understanding of their challenges, which leads to innovative solutions and strong ROI. Long-term collaborations—some over a decade—demonstrate their trust and satisfaction. Their success stories drive us to continually exceed expectations. [Know More **](#quote-form) ![](/template/ooitech/assets/img/icon/quote.svg) A man with a big soul. Thank you very much for your visit Mr Wu. Thank you very much for the services provided in installing equipment and training my students. The kindest person and professional in his field ![](https://cdn.ooitech.com/runtime/image/w800_h600_fitblur_v2_2026041716444445.webp) ### Jizzakh Polytechnic Institute ![](/template/ooitech/assets/img/icon/quote.svg) Thanks to Ooitech for providing highly suitable BC solar cell experimental equipment. ![](https://cdn.ooitech.com/runtime/image/w800_h600_fitblur_v2_1776426122864564.webp) ### KTECH ![](/template/ooitech/assets/img/icon/quote.svg) Thank you again so much again for the very big big help for improving and fixing the factory and also teaching the workers how to use the machines ![](https://cdn.ooitech.com/runtime/image/w800_h600_fitblur_v2_1757479675272137.webp) ### Mark BIPV Philippines ![](/template/ooitech/assets/img/icon/quote.svg) Thanks to Ooitech for providing the fully automated production equipment—your installation and after-sales service have been excellent. ![](https://cdn.ooitech.com/runtime/image/w800_h600_fitblur_v2_2026041720921238.webp) ### Amjad ## Our Latest Products ![Interconnection Busbar – Solar Cell String Current Collection](https://cdn.ooitech.com/runtime/image/w800_h600_fitblur_v2_2026032713037538.jpg.webp) - [** Rachael](/Interconnection-Busbar-for-Solar-Module-Assembly-High-Performance-Current-Collection-Solution.html) - [** 96326](/Interconnection-Busbar-for-Solar-Module-Assembly-High-Performance-Current-Collection-Solution.html) ### Interconnection Busbar – Solar Cell String Current Collection Premium interconnection busbar solutions for solar module assembly, featuring high-purity tinned copper construction, optimized cross-sectional design for minimal power loss, and reliable current collection from cell strings to junction boxes. Essential c ![BD03 Frame Gluing Machine – Aluminum Frame Sealant System](https://cdn.ooitech.com/runtime/image/w800_h600_fitblur_v2_1774506308732524.webp) - [** Rachael](/Offline-Frame-Gluing-Machine-BD03-Professional-Aluminum-Frame-Sealant-Application-System.html) - [** 51530](/Offline-Frame-Gluing-Machine-BD03-Professional-Aluminum-Frame-Sealant-Application-System.html) ### BD03 Frame Gluing Machine – Aluminum Frame Sealant System BD03 CNC frame gluing machine – automated aluminum frame sealant application with precise positioning, automatic feeding and uniform glue distribution for solar panel production lines. ![Solar Panel Tester Sun Simulator OTMT-A | AAA Class Solar Module IV Tester | Ooitech](https://cdn.ooitech.com/runtime/image/w800_h600_fitblur_v2_1774513832212306.jpg) - [** ooitech](/solar-panel-tester-sun-simulator-otmt-a-aaa-class-solar-module-iv-tester-ooitech.html) - [** 318](/solar-panel-tester-sun-simulator-otmt-a-aaa-class-solar-module-iv-tester-ooitech.html) ### Solar Panel Tester Sun Simulator OTMT-A | AAA Class Solar Module IV Tester | Ooitech Ooitech OTMT-A Solar Panel Tester Sun Simulator is an AAA class solar module IV testing system featuring xenon lamp technology, IEC 60904-9 compliance, ±2% light non-uniformity, and 300,000 flash lamp life. Ideal for mono-Si and poly-Si solar panel produc ![Solar Junction Box – Bypass Diode, IP67, PV Module Output](https://cdn.ooitech.com/runtime/image/w800_h600_fitblur_v2_2026032739568544.jpg.webp) - [** Rachael](/Solar-Junction-Box-J-Box-Advanced-PV-Module-Protection-Power-Management-System.html) - [** 13943](/Solar-Junction-Box-J-Box-Advanced-PV-Module-Protection-Power-Management-System.html) ### Solar Junction Box – Bypass Diode, IP67, PV Module Output Solar junction box with bypass diodes & IP67/IP68 rating – hot spot protection, MC4 connectors, optional smart monitoring. 25+ year reliability for all solar module types and climates. ![Junction Box Welding Machine KS-01C | Automatic Solar Panel Junction Box Soldering Equipment - Ooitech](https://cdn.ooitech.com/runtime/image/w800_h600_fitblur_v2_1774492507915923.webp) - [** Rachael](/junction-box-welding-machine-ks-01c-automatic-solar-panel-junction-box-soldering-equipment-ooitech.html) - [** 92012](/junction-box-welding-machine-ks-01c-automatic-solar-panel-junction-box-soldering-equipment-ooitech.html) ### Junction Box Welding Machine KS-01C | Automatic Solar Panel Junction Box Soldering Equipment - Ooitech Ooitech KS-01C Junction Box Welding Machine features automatic hot bar tin welding and high frequency welding with CCD positioning accuracy of ±0.1mm. Supports 5BB-12BB full cell, half-cut, and bifacial modules. Cycle time ≤16s with 99.6% welding quality ![Solar Panel EL Tester & VI Tester Machine OPT-M960B M951B M950B | Ooitech Solar Module EL Testing Equipment](https://cdn.ooitech.com/runtime/image/w800_h600_fitblur_v2_1774351816741704.webp) - [** Rachael](/solar-panel-el-tester-and-vi-tester-machine-opt-m960b-m951b-m950b-ooitech-solar-module-el-testing-equipment.html) - [** 43207](/solar-panel-el-tester-and-vi-tester-machine-opt-m960b-m951b-m950b-ooitech-solar-module-el-testing-equipment.html) ### Solar Panel EL Tester & VI Tester Machine OPT-M960B M951B M950B | Ooitech Solar Module EL Testing Equipment Ooitech offers professional solar panel EL tester and VI tester machines (OPT-M960B, OPT-M951B, OPT-M950B) with SONY industrial cameras, automatic image mosaicing, MES interfacing, and high-precision electroluminescence and visual inspection for solar mod