# EPE Encapsulant Lamination Delamination: Line-Shaped Bubbles Along Solar Cell Ribbons - - Ooitech, the world's leading solar panel production line solutions provider, supply chain expert, solar panel making machine facotry > A technical blog explaining why EPE encapsulant may cause lamination delamination and line-shaped bubbles along solar cell ribbons, with analysis of additive migration, crosslinking mismatch, thermal expansion stress, and practical process control suggest ![EPE Encapsulant Lamination Delamination: Line-Shaped Bubbles Along Solar Cell Ribbons](https://cdn.ooitech.com/static/upload/image/20260703/2cca1179af58f4d5696fe713c36abf12.webp) - ** 2026-07-03 - ** 0 Views - ** [Blog](/Blog.html) ### EPE Encapsulant Lamination Delamination: Line-Shaped Bubbles Along Solar Cell Ribbons ##### Introduction: What Is EPE Encapsulant Film? EPE encapsulant film, also known as co-extruded POE encapsulant, is a photovoltaic encapsulation material produced by co-extruding POE resin and EVA resin. In solar module manufacturing, it is mainly used to combine the processing convenience of EVA with the moisture-barrier and anti-PID performance of POE. Conventional EVA film is widely used in PV module production because it offers good anti-PID performance, high light transmittance, UV and damp-heat yellowing resistance, snail-trail resistance, and strong adhesion to glass and backsheet. However, EVA also has limitations, such as relatively weak moisture barrier performance, higher water vapor transmission, and a higher risk of PID under certain operating conditions. POE film, by comparison, has a better water vapor barrier, stronger weather resistance, and more reliable anti-PID capability. But POE also has its own processing challenges: its adhesion to glass and backsheet is usually weaker than EVA, its crosslinking reaction is slower, and during module production the film may slip or shift more easily, which can reduce production efficiency. This is why EPE film was developed. Through a co-extrusion process, POE is wrapped by EVA layers, forming an EVA-POE-EVA sandwich structure. This design keeps the **high moisture barrier** of POE, helping protect solar cells from water vapor, while also maintaining the **good lamination compatibility and easier processability** of EVA. In normal production, EPE can improve both module reliability and manufacturing yield when the material and lamination process are well controlled. ##### Technical Mechanism: Why EPE May Delaminate During Lamination Although EPE combines the advantages of EVA and POE, the two materials do not behave exactly the same during lamination. Their curing curves, crosslinking characteristics, polarity, additive absorption ability, and thermal expansion behavior are different. These differences may lead to interlayer delamination and bubble formation, especially around solder ribbon areas where local pressure and thickness variation are more obvious. EVA and POE have different polarity. EVA is a polar material, so it has good compatibility with many additives. POE is less polar, so its ability to retain polar additives is different. Over storage time, additives inside the POE layer may gradually migrate toward the EVA layers, which have stronger polarity and better absorption capability. This additive migration changes the internal structure and performance of the EPE film. As a result, the bonding force between the POE and EVA layers may decrease. In severe cases, the POE layer may be squeezed, separated, or locally delaminated during module lamination. This is also one reason why the shelf life of EPE film is generally shorter than that of single EVA or single POE encapsulant film. | Key Factor | Mechanism | Possible Defect in Module Lamination | | --- | --- | --- | | Additive migration | Polar additives such as crosslinking agents and stabilizers migrate from POE to EVA over time | Lower POE crosslinking degree, reduced cohesion, EPE interlayer delamination | | Crosslinking speed mismatch | EVA usually crosslinks faster than POE during lamination | EVA layer becomes solid earlier while POE remains molten, causing interlayer stress imbalance | | Thermal expansion coefficient difference | EVA and POE show different expansion and shrinkage behavior after curing | Internal stress during cooling, possible interlayer separation | | Local thickness variation | POE layer thickness may be uneven in the TD direction, or EPE becomes locally thinner near ribbons and busbars | Local glue shortage, gas accumulation, line-shaped bubbles | | Ribbon and busbar overlap pressure | Local stack thickness is higher at soldering positions | Encapsulant flow, local delamination, linear bubbles extending from ribbon areas | ##### Technical Analysis: Formation of Line-Shaped Bubbles Along Ribbons The line-shaped bubbles extending from solder ribbons are often related to the combined effect of additive migration, inconsistent crosslinking speed, and different thermal expansion behavior between EVA and POE. During lamination, EVA crosslinks faster than POE. If the POE layer does not crosslink in time, reaction gases generated during peroxide decomposition may not be fully discharged before pressure is applied. These gases can remain trapped inside the module and form bubbles. Another common reason is local thinning of the EPE film at the ribbon and busbar positions. The middle POE layer of EPE may have thickness non-uniformity in the TD direction due to raw material factors. In addition, during lamination, the overlapping thickness of ribbons and busbars increases local pressure. This can make EPE thinner at that position, creating a weak point where adhesive shortage or gas accumulation is more likely. In simple terms, the ribbon area receives higher pressure during lamination. If the EVA layers have already started to crosslink while the POE layer near the ribbon is still in a flowing state, the EPE structure may locally separate. The remaining encapsulant at the ribbon position may behave more like POE, with slower crosslinking and higher flow tendency. Under lamination pressure, this can create colored or transparent line-shaped bubbles spreading outward from the ribbon. ###### Key process symptoms to watch - Bubbles appear mainly along solder ribbon paths rather than randomly across the whole module. - The defect may look like thin linear air traces extending outward from ribbon or busbar areas. - The problem may become more obvious when EPE film has been stored for a longer time. - The defect may increase when lamination temperature, vacuum time, pressure timing, or curing degree are not well matched with the specific EPE formulation. ##### Practical Control Suggestions for EPE Lamination Defects For bubbles caused by the inherent material behavior of EPE encapsulant, the solution should combine material management and lamination process optimization. It is not enough to adjust only one parameter without checking the film storage condition, lamination curve, and ribbon-area pressure distribution. ###### 1. Control EPE material storage time Plan EPE encapsulant procurement and production usage carefully. Under the condition that production is not affected, reduce the inventory time of EPE film as much as possible. Shorter storage time helps reduce additive migration from the POE layer to EVA layers, keeping the original interlayer bonding and crosslinking behavior more stable. ###### 2. Properly increase the first-chamber lamination temperature A suitable increase in the first-chamber lamination temperature can accelerate POE crosslinking in the EPE film. This helps avoid the situation where EVA has already reached a relatively high crosslinking degree while POE is still molten. Better synchronization between EVA and POE curing can reduce interlayer stress and help prevent line-shaped bubbles near ribbon positions. ###### 3. Match vacuum, pressure, and curing timing If pressure is applied too early while the POE layer is still highly fluid, gas may be trapped or pushed along ribbon areas. A well-designed lamination recipe should allow enough time for air extraction and material softening before full pressure is applied. The exact setting should be verified by crosslinking degree tests, peel strength tests, and appearance inspection after lamination. ###### 4. Check ribbon and busbar stack height Because local pressure is higher around ribbons and busbars, excessive stack thickness can make EPE thinner at these points. Production teams should check soldering flatness, ribbon alignment, busbar overlap, and layup consistency. Reducing local height difference can lower the risk of local encapsulant deformation and bubble formation. ###### 5. Verify incoming EPE quality For EPE film, incoming inspection should not only check appearance and thickness, but also focus on thickness uniformity, shelf life, storage condition, gel content behavior, and adhesion performance. If possible, trial lamination should be done before mass production when changing suppliers, batches, or module structures. This blog is based on practical abnormality analysis in PV module production and the following references: 1. Field experience from abnormal defect analysis during photovoltaic module production 2. Dow Chemical, Zhang Wenxin, "POE Empowering High-Performance Photovoltaic Modules" 3. Southwest Securities, "N-Type Iteration, POE Industry Opens a High-Growth Cycle" 4. Chemical Production and Technology, "Research on Crosslinking Reaction of Polyolefin Encapsulant Film for Photovoltaics" ##### Ooitech's View As an equipment supplier, we see it this way: EPE-related ribbon line bubbles are not only a material issue, but also a process-window issue that depends on lamination temperature profile, vacuum efficiency, pressure timing, and layup flatness. For module manufacturers using advanced cell technologies and larger formats, the tolerance for encapsulant flow and local stack height becomes much smaller, so material shelf-life control and lamination recipe validation should be treated as part of the same quality system. A stable solar panel production line needs both good encapsulant selection and disciplined process verification before mass production. --- ##### Tags : ![](/template/ooitech/assets/img/shape/06.png) ![](https://cdn.ooitech.com/static/upload/image/20250909/1757399770541443.webp) ### Request A Quote All uploads are secure and confidential. ## We deliver expertise you can trust our service Direct-from-Factory Equipment. ![](/template/ooitech/assets/img/icon/money-2.svg) ### Cost-Effective Advantages We deliver exceptional value, maximizing results while optimizing budgets for clients. ![](/template/ooitech/assets/img/icon/staff.svg) ### Our Experience Team Our skilled professionals specialize in innovative solutions and tailored strategies. ![](/template/ooitech/assets/img/icon/certified.svg) ### 15+ Years Industry Experience Deep expertise ensures reliable, trend-aware, and proven outcomes for success. ![](https://cdn.ooitech.com/static/upload/image/20250910/1757477357667605.webp ) ![](https://cdn.ooitech.com/static/upload/image/20250910/1757477724911512.webp) ![](/template/ooitech/assets/img/shape/06.png) ## What Our Client Say's about us Client testimonials praise our deep understanding of their challenges, which leads to innovative solutions and strong ROI. Long-term collaborations—some over a decade—demonstrate their trust and satisfaction. Their success stories drive us to continually exceed expectations. [Know More **](#quote-form) ![](/template/ooitech/assets/img/icon/quote.svg) A man with a big soul. Thank you very much for your visit Mr Wu. Thank you very much for the services provided in installing equipment and training my students. The kindest person and professional in his field ![](https://cdn.ooitech.com/runtime/image/w800_h600_fitblur_v2_2026041716444445.webp) ### Jizzakh Polytechnic Institute ![](/template/ooitech/assets/img/icon/quote.svg) Thanks to Ooitech for providing highly suitable BC solar cell experimental equipment. ![](https://cdn.ooitech.com/runtime/image/w800_h600_fitblur_v2_1776426122864564.webp) ### KTECH ![](/template/ooitech/assets/img/icon/quote.svg) Thank you again so much again for the very big big help for improving and fixing the factory and also teaching the workers how to use the machines ![](https://cdn.ooitech.com/runtime/image/w800_h600_fitblur_v2_1757479675272137.webp) ### Mark BIPV Philippines ![](/template/ooitech/assets/img/icon/quote.svg) Thanks to Ooitech for providing the fully automated production equipment—your installation and after-sales service have been excellent. ![](https://cdn.ooitech.com/runtime/image/w800_h600_fitblur_v2_2026041720921238.webp) ### Amjad ## Our Latest Products ![OSLB-1300 Back Contact Cell Welding Machine | BC Solar Cell Stringer for IBC ABC HPBC Panel Production](https://cdn.ooitech.com/runtime/image/w800_h600_fitblur_v2_2026032311945973.png) - [** ooitech](/oslb-1300-back-contact-cell-welding-machine-bc-solar-cell-stringer-for-ibc-abc-hpbc-panel-production.html) - [** 98610](/oslb-1300-back-contact-cell-welding-machine-bc-solar-cell-stringer-for-ibc-abc-hpbc-panel-production.html) ### OSLB-1300 Back Contact Cell Welding Machine | BC Solar Cell Stringer for IBC ABC HPBC Panel Production OSLB-1300 back contact cell welding machine by Ooitech delivers ≥1000 cells/hour throughput for BC, IBC, ABC, and HPBC solar cell string welding. Features A/B dual cell loading, CCD + SCARA robot positioning (±0.2mm), infrared heating welding, inline EL i ![HDX200-P Half Cell Auto Bussing Machine | Automatic Busbar Welding Machine for Solar Panel Production](https://cdn.ooitech.com/runtime/image/w800_h600_fitblur_v2_1774341533138807.webp) - [** Rachael](/hdx200-p-half-cell-auto-bussing-machine-automatic-busbar-welding-machine-for-solar-panel-production.html) - [** 84341](/hdx200-p-half-cell-auto-bussing-machine-automatic-busbar-welding-machine-for-solar-panel-production.html) ### HDX200-P Half Cell Auto Bussing Machine | Automatic Busbar Welding Machine for Solar Panel Production HDX200-P Half Cell Auto Bussing Machine features electromagnetic induction welding with 18 welding heads, cycle time under 18 seconds, and over 99% yield rate. Compatible with 156-230mm solar cells and 5-30 busbars, supporting PERC, TOPCon, and HJT half-c ![Automatic Tape Sticking Machine for Solar Panel Production Line | Ooitech](https://cdn.ooitech.com/runtime/image/w800_h600_fitblur_v2_1774350079476146.webp) - [** Rachael](/automatic-tape-sticking-machine-for-solar-panel-production-line-ooitech.html) - [** 81357](/automatic-tape-sticking-machine-for-solar-panel-production-line-ooitech.html) ### Automatic Tape Sticking Machine for Solar Panel Production Line | Ooitech Ooitech Automatic Tape Sticking Machine applies adhesive tape on solar cell strings with high precision and speed. Features 2 or 4 tape heads, cycle time ≤25s, ±2mm accuracy, MES compatible, fully automatic operation for solar panel production lines. ![Interconnection Busbar – Solar Cell String Current Collection](https://cdn.ooitech.com/runtime/image/w800_h600_fitblur_v2_2026032713037538.jpg.webp) - [** Rachael](/Interconnection-Busbar-for-Solar-Module-Assembly-High-Performance-Current-Collection-Solution.html) - [** 96262](/Interconnection-Busbar-for-Solar-Module-Assembly-High-Performance-Current-Collection-Solution.html) ### Interconnection Busbar – Solar Cell String Current Collection Premium interconnection busbar solutions for solar module assembly, featuring high-purity tinned copper construction, optimized cross-sectional design for minimal power loss, and reliable current collection from cell strings to junction boxes. Essential c ![Full Automatic Solar Panel Production Line Equipment | Ooitech](https://cdn.ooitech.com/runtime/image/w800_h600_fitblur_v2_1774401482439949.webp) - [** Rachael](/full-automatic-solar-panel-production-line-equipment-ooitech.html) - [** 98187](/full-automatic-solar-panel-production-line-equipment-ooitech.html) ### Full Automatic Solar Panel Production Line Equipment | Ooitech Ooitech full automatic solar panel production line covers glass loading, EVA laying, string layout, tape sticking, lamination, trimming, framing, junction box soldering, gluing, grinding, testing and sorting. Compatible with PERC, TOPCon, IBC, bifacial, h ![Solar Panel Frame Removal Machine – Auto Deframing Equipment](https://cdn.ooitech.com/runtime/image/w800_h600_fitblur_v2_1774608027244403.webp) - [** Rachael](/Solar-Panel-Frame-Removal-Machine-High-Efficiency-Automated-Deframing-Equipment.html) - [** 73195](/Solar-Panel-Frame-Removal-Machine-High-Efficiency-Automated-Deframing-Equipment.html) ### Solar Panel Frame Removal Machine – Auto Deframing Equipment Hydraulic solar panel frame removal machine – automated deframing for PV module recycling. Low breakage, supports multiple panel sizes. Efficient disassembly for solar module refurbishment lines.